LT9-450Copper Large Pull with continuous annealing production line
copper rod breakdown machine;rod breakdown machine;8mm copper rod dawing machine
From 8mm to 1.78mm—3.30mm
copper rod input diameter:8mm,
output diameter: 1.78mm—3.30mm
production speed:480meters/s
production capacity: 1200KG/hour
copper rod breakdown wire drawing machine (450/LT9)
number of dies:9
installed capacity:125KVA (Main motor:AC.110KW,spooler motor:15KW)
drive: frequency inverters
Dimension length 3000 * 1800mm Weight 6.5T width
This company produces LT9-450 continuous annealing line used with pull-plus double-disc received Continuous Annealing Line (or, as the nose unloading line) production model, the formation of the entire production line continuous operation, drawing machine from a copper rod into the line of direct pull 8.00mm Model copper wire.
Annealing mode DC-annealing, annealing the use of advanced low-voltage power supply high current power supply, the control system adopts microcomputer intelligent control, equipment operation more stable, the maximum speed of 8 m / sec.
| Wire drawing bench | |||
|---|---|---|---|
| parameters | 350water tank wire drawing | 450water tank wire drawing | |
| Inlet diameter | Φ3mm | Φ8mm | |
| Outlet diameter | Φ0.8-Φ2.8mm | Φ2.2-Φ3..3mm | |
| Drawing speed | 400m/min | 380m/min | |
| Main motor power | AC 22Kw－37Kw | DC 110Kw－160Kw | |
| Take-up machine power | Torque motor 20A 6P | Torque motor 25A 6P | |
| weight | 1000Kg | 6000Kg | |
| Annealing machine | |||
| parameters | TH－800 | TH－1200 | |
| Annealing wire diameter range | 0.8－2.8mm | 2.2－3.3mm | |
| maximum speed | 380m/min (Φ2.0mm) | 360m/min (Φ2.5mm) | |
| Annealing current | 1500A | 2000A | |
| Annealing voltage | 50V | 50V | |
| Annealing capacity | 60KVA | 100KVA | |
| Shape size （long×width×height） | 1500×750×2000 | 1600×750×2000 | |